Glossy white PVC film 80µm on SP123 super-permanent adhesive and white kraft liner 130gsm.
Facestock
PVC Gloss White
Monomeric plasticised polyvinyl-chloride film with good dimensional stability.
Technical data
| Property | Norm | Units | Value | Tolerance |
| Substance | ASTM D 1593 | g/m² | 110 | 104.4 - 115.4 |
| Thickness | ASTM D 1593 | µm | 80 | 72-88 |
| Gloss 60º | ASTM D 523 | % | > 80 | ≥ 65 |
| Surface tension | DIN 53364 | dina/cm | ≥ 36 | |
| Dimensional stability 100ºC 10min MD | ASTM D 1204 | % | -5 | 5 |
| Dimensional stability 100ºC 10min CD | ASTM D 1204 | % | -2 | ± 2 |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline
Adhesive
SP123
Acrylic super-permanent adhesive with high tack. For difficult surfaces such as wood, some cardboards and plastics such as HDPE, PP, PET and PVC.
Technical data
| Property | Norm | Units | Value | Tolerance |
| Adhesion (Peel 180º 20'/stainless steel) | FTM 1 | N/25mm | 17,2 | ≥ 13,5 |
| Tack (Quick Stick stainless steel) | FTM 9 | N | 11 | ≥ 9,8 |
| Shear (1kg, in²/glass) | FTM 8 | min | 100 | ≥ 60 |
| Minimum labelling temperature | | ºC | +5 | |
| Minimum service temperature | | ºC | -20 | |
| Maximum service temperature. | | ºC | +80 | |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline
Liner
Kraft White 130
One-side coated white liner with high stiffness and stability. Available in split and solid back.
Technical data
| Property | Norm | Units | Value | Tolerance |
| Substance | ISO 536 | g/m² | 130 | 124,8 - 135,2 |
| Thickness | ISO 534 | µm | 134 | 124 - 144 |
| Tensile strength MD/CD | ISO 1924-2 | kN/m | ≥6,7 / ≥4,3 | |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline
Download complete product sheet
|